，平均表粗小於1.5 搭配快速退火程序，可將正極膜層之體積電容量有效提

，平均表粗小於1.5 搭配快速退火程序，可將正極膜層之體積電容量有效提升至52 Ah/mcm2以上，達成本計畫預期階段目標。

結果 (英文) 1:

, the average surface roughness is less than 1.5. With the rapid annealing process, the volume capacitance of the positive electrode film layer can be effectively increased to more than 52 Ah/mcm2, achieving the expected stage goal of this project.

結果 (英文) 2:

With an average surface thickness of less than 1.5 and a rapid annealing program, the volume electrical capacity of the positive electrode film layer can be effectively increased to over 52 μ Ah/μ m ∙ cm2, achieving the expected stage goal of the cost plan.

結果 (英文) 3:

With the average surface roughness less than 1.5 and rapid annealing process, the volume capacitance of the positive electrode film can be effectively increased to more than 52 Ah/mcm2, reaching the expected stage goal of the project.